Structural heredity in amorphous alloy Fe81B13Si4C2 / Kataev VA,Letov MV,Starodubtsev YN,Tsepelev VS,Kuzevanova LA // PHYSICS OF METALS AND METALLOGRAPHY. - 2001. - V. 92, l. 2. - P. 123-127.

ISSN/EISSN:

0031-918X / нет данных

Type:

Article

Abstract:

Effect of the duration of annealing at 380 degreesC on the structural state and magnetic properties of the Fe81B13Si4C2 alloy was investigated in some detail. The amorphous ribbons of the alloy were obtained using two technological variants: with an overheating and without overheating of the melt above the critical temperature. The samples of ribbons that were obtained with overheating exhibited higher magnetic properties after an optimum annealing duration. The magnetic properties of alloy samples that were obtained without overheating decrease sharply after holding for 20 min. The results obtained, on the one hand, indicate the presence of the effect of structural heredity and, on the other hand, indicate a way of significant improvement of the time-temperature stability of this alloy and products made of this alloy.

Author keywords:

FERROMAGNETS

DOI:

нет данных

Web of Science ID:

ISI:000171358200004

Соавторы в МНС:

Другие поля

Поле	Значение
Month	AUG
Publisher	INTERPERIODICA
Address	PO BOX 1831, BIRMINGHAM, AL 35201-1831 USA
Language	English
Keywords-Plus	FERROMAGNETS
Research-Areas	Metallurgy \& Metallurgical Engineering
Web-of-Science-Categories	Metallurgy \& Metallurgical Engineering
Number-of-Cited-References	6
Journal-ISO	Phys. Metals Metallogr.
Doc-Delivery-Number	478RB