Coercive-force and eddy-current testing of the abrasive wear resistance of quenched and tempered hypereutectoid carbon steels: II. Steels subjected to different quenching regimes, subzero treatment, and tempering after high-temperature quenching / Makarov A. V.,Gorkunov E. S.,Kogan L. Kh.,Kolobylin Yu. M. // RUSSIAN JOURNAL OF NONDESTRUCTIVE TESTING. - 2007. - V. 43, l. 5. - P. 288-301.

ISSN/EISSN:

1061-8309 / нет данных

Type:

Article

Abstract:

The effects of the carbon concentration in martensite from 0.70 to 1.35 wt \%, the presence of up to 70 vol \% residual austenite, the degree of coagulation, and the volume fraction of tempering carbides on the specific features of the application of eddy-current and magnetic methods for testing abrasive wear resistance are studied. The case of high-carbon (0.83-1.53 wt \% C) steels quenched from 790-1200 degrees C, treated with cold at -196 degrees C, and tempered in the temperature range 75-700 degrees C is considered.

Author keywords:

нет данных

DOI:

10.1134/S1061830907050026

Web of Science ID:

ISI:000249271200002

Соавторы в МНС:

—

Другие поля

Поле	Значение
Month	MAY
Publisher	MAIK NAUKA/INTERPERIODICA/SPRINGER
Address	233 SPRING ST, NEW YORK, NY 10013-1578 USA
Language	English
Research-Areas	Materials Science
Web-of-Science-Categories	Materials Science, Characterization \& Testing
ResearcherID-Numbers	Kolobylin, Yury/D-6083-2016 Leonid, Kogan/J-8150-2013 Makarov, Aleksey/D-5663-2016 Горкунов, Эдуард/D-5091-2016
ORCID-Numbers	Kolobylin, Yury/0000-0002-7831-2624 Leonid, Kogan/0000-0003-2725-3748 Makarov, Aleksey/0000-0002-2228-0643 Горкунов, Эдуард/0000-0003-1820-2746
Number-of-Cited-References	4
Usage-Count-Since-2013	2
Journal-ISO	Russ. J. Nondestr. Test.
Doc-Delivery-Number	207SK